Progress in modelling solidification microstructures in metals and alloys. Part II: dendrites from 2001 to 2018

This is the first account of the history of modelling dendritic and cellular solidification. While Part I reviewed the progress up to the year 2000 [Kurz W, Fisher DJ, Trivedi R. Progress in modelling solidification microstructures in metals and alloys: de ...

TAYLOR & FRANCIS LTD2021

Measurement of Mechanical Coherency Temperature and Solid Volume Fraction in Al-Zn Alloys Using In Situ X-ray Diffraction During Casting

Jean-Marie Drezet, Güven Kurtuldu, Bastien Gilbert Pierre Mireux

During solidification of metallic alloys, coalescence leads to the formation of solid bridges between grains or grain clusters when both solid and liquid phases are percolated. As such, it represents a key transition with respect to the mechanical behavior ...

Springer Verlag2015

In situ X-ray Diffraction during Casting: Study of Hot Tearing in Al-Zn alloys

Jean-Marie Drezet, Güven Kurtuldu, Bastien Gilbert Pierre Mireux

During solidification of metallic alloys, coalescence corresponds to the formation of solid bridges between grains when both solid and liquid phases are percolated. As such, it represents a key transition with respect to the mechanical behaviour of solidif ...

Trans Tech Publications Switzerland2015

Neutron Diffraction Measurement of As-Cast Residual Stresses in Aa7050 Rolling Plate Ingots: Influence of A Wiper

Jean-Marie Drezet

During casting, thermally induced deformations give birth to ingot distortions and residual stresses. For some high strength alloys, ingot cracking can happen during casting per se or during cooling down. Ingot distortions such as rolling face pull-in, but ...

John Grandfield2014

Influence of microstructural heterogeneity on the scaling between flow stress and relative density in microcellular Al-4.5 %Cu

Andreas Mortensen, Yves Conde

We explore the influence of the metal microstructure on the compressive flow stress of replicated microcellular 400-mu m pore size Al-4.5 wt%Cu solidified at two different solidification cooling rates, in the as-cast and T6 conditions. It is found that the ...

Springer Verlag2014

Characterization and modeling of twinned dendrite growth

Mario Alberto Salgado Ordorica

The formation of feathery grains during semi-continuous casting of Al-alloys [1, 2] is an interesting problem from both practical and theoretical points of view. These structures are formed by a lamellar sequence of twinned and untwinned regions separated ...

EPFL2009

Application of the Rappaz-Drezet-Gremaud Hot Tearing Criterion to Welding of Aluminium Alloys

Jean-Marie Drezet

Hot tearing, a severe defect occurring during solidification is the conjunction of tensile stresses which are transmitted to the mushy zone by the coherent solid underneath and of insufficient liquid feeding to compensate for the volumetric change. The RDG ...

Springer2008

Effects of edge defects induced by multi-wire sawing on the wafer strength

Christophe Ballif, Mathijs Pieter van der Meer, Adrien Bidiville, Fanny Alexia Jeanneret

The focus of the photovoltaic industry is a continuous reduction of the cost of solar energy. Lowering the wafer thickness during the processing by means of multi-wire slurry saw technology is one of the key issue to reduce these costs. However, reducing t ...

2008