AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.
The objective of this thesis is to improve methods for predicting the fatigue life, multiaxial or not, of mild- and more particularly high-strength steels using local approaches that have the capacity to be applicable to almost any cases, hence the term ge ...
Fiber-reinforced polymer (FRP) composite materials are currently being selected for the design of lightweight and efficient structural members in a wide number of engineering applications. Sandwich panels with glass fiber-reinforced polymer (GFRP) face she ...
Cast-in-place thin layers of Ultra-High Performance Fiber Reinforced Cementitious Composites (UHPFRC) on the specific zones of existing reinforced concrete (RC) bridge decks has been demonstrated to be a technically efficient and economic rehabilitation an ...
High-head steel lined pressure tunnels and shafts may be considered as critical infrastructures especially when rock overburden is small. In the case of lining failure, catastrophic damages can occur when a large amount of water can reach the steep valley ...
Dry-snow slab avalanches release due to the formation of a crack in a weak layer buried below cohesive snow slabs, followed by rapid crack propagation. The onset of rapid crack propagation occurs if stresses at the crack tip in the weak layer overcome its ...
The case study of the fatigue safety examination of the 120 years old steel riveted bridge carrying a single railway track on two main girders is presented. The overall assessment according to the Swiss Standard SIA 269 for existing structures indicated su ...
The 2D delamination behavior of composite laminates under quasi-static out-of-plane opening loading has been experimentally investigated. A circular embedded pre-crack was introduced in the center and at the midplane of the laminates. To investigate the ef ...
As fatigue cracks were discovered under the bridge deck of the 48 years old railway bridge Linthkanal-Brücke, located near the Ziegelbrücke town in Switzerland, a few studies were conducted to understand the mechanism behind the cracks formation. However, ...
Today, it is widely accepted that fatigue is one of the most common failure mechanisms in structural components, and pure static failure is rarely observed. Engineering structures are subjected to complex mechanical fatigue loading histories, which cause d ...
The effect of load interruptions on the fatigue behavior of (±45)2s angle-ply glass/epoxy composite laminates was investigated in this work. Constant amplitude fatigue experiments were performed at different stress levels to derive base line fatigue data. ...