Effect of Loading Pattern on Fatigue Behavior of Laminated Composites

Résumé

The effect of load interruptions on the fatigue behavior of (±45)2s angle-ply glass/epoxy composite laminates was investigated in this work. Constant amplitude fatigue experiments were performed at different stress levels to derive base line fatigue data. In addition, interrupted-fatigue experiments were performed by removing the cyclic loading for two hours repetitively, after cycling for 20% of the fatigue life achieved under continuous loading at the same maximum cyclic stress level. The specimens loaded under interrupted fatigue exhibited longer fatigue live than those continuously loaded until failure

À propos de ce résultat
Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Graph Chatbot

Chattez avec Graph Search

Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.

AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.