Anodic oxidation of phenol on Ti/IrO2 electrode: Experimental studies

Stéphane Fierro
Elsevier, 2010
Article

Résumé

The electrochemical oxidation of acidic solutions of phenol on a Ti/IrO2 anode has been investigated by cyclic voltammetry and bulk electrolysis in a single-compartment cell. In the potential region of oxygen evolution, anodic oxidation resulted in electrode passivation (as evidenced by voltammetric measurements) allegedly due to the formation of a polymeric film on its surface. Phenol degradation increased with increasing temperature in the range investigated 30-80 degrees C and it was affected by the addition of Cl- and Br- anions in the supporting electrolyte. Complete conversion of 10 mM phenol was achieved after 37 Ah L-1 of charge passed at 80 degrees C under galvanostatic conditions (50 mA cm(-2)) in absence of Cl-. In contrast only 10 Ah L-1 were needed in the presence of 35 mM Cl-. The presence of chloride can induce reactions involving chlorohydroxyl radicals and electrogenerated oxidants such as free chlorine. On the other hand, addition of Br- slightly inhibited degradation possibly due to bromide scavenging of electrogenerated active species. Phenol degradation proceeded through the formation of three dominant, aromatic intermediates, namely 1,4-benzoquinone, hydroquinone and pyrocatechol, while total oxidation to CO2 was not significant unless harsh conditions (i.e. high temperatures and charges) were employed. (C) 2010 Elsevier B.V. All rights reserved.

Official source

https://infoscience.epfl.ch/record/149771?ln=fr

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Concepts associés

Chargement

Publications associées

Chargement

Dimensionally Stable Anodes (DSA®) are electrodes composed of a metal support and an oxide coating (catalyst). Particularly in this thesis, the Ti/IrO2 electrode was used for the study of the fraction of the surface which participates effectively in the investigated reactions (effectiveness factor, Ef ). Four reactions with different kinetics have been investigated: (a) Fe3+/Fe2+ (fast reaction), (b) O2 and (c) Cl2 evolutions (slow reactions), and (d) isopropanol oxidation (complex reaction involving redox catalysis). This study has allowed us to apply for the first time in electrocatalysis the term, effectiveness factor, Ef , used before in other fields like in heavy metals recovery with 3D electrodes and in heterogeneous catalysis. On the other hand, in order to achieve the main objective of this thesis, an analytical and a qualitative approach was proposed. Furthermore, the Ti/IrO2 electrodes were characterized electrochemically using the cyclic voltammetry (CV) technique in which the voltammetric charge was measured at different potential scan rates, potential windows, and electrolyte temperatures using various Ti/IrO2 loadings. From the voltammetric charge, two contributions were found. The first contribution is related to the double layer capacitance and the second with the redox couples present on the electrode surface. The first reaction investigated in this work was the Fe3+/Fe2+ redox couple. In the first part of the investigation of this reaction, the CV technique was used; however, some issues related to the uncompensated electrolyte resistance were encountered. Therefore the effectiveness factor for this particular case was not possible to obtain. On the other hand, using rotating Ti/IrO2 disk electrodes (RDE) for the same reaction, the effectiveness factor, Ef , has been estimated, however, this value is much lower than the predicted one. The other investigated reactions in this work were O2 and Cl2 evolutions. The investigated kinetics of both reactions showed that the evolution of chlorine is much faster than that of oxygen. The effectiveness factor, Ef , for the oxygen evolution was close to the unity for all IrO2 loadings, contrary to the chlorine reaction that decreased with the loading. This behaviour was predicted according to what is given in the analytical approach. The last reaction investigated in this work was the oxidation of isopropanol. In this case a model was proposed based on three main reactions: Electrochemical IrO2 oxidation to IrO3, chemical oxidation of isopropanol via IrO3, and chemical decomposition of IrO3 to IrO2. The effectiveness factor, for the electrochemical reaction seemed not to correlate with the loading, whereas for the chemical one, it diminished with the loading.

EPFL2008

Chargement

Electrochemical oxidation of phenol at boron-doped diamond electrode. Application to electro-organic synthesis and wastewater treatment

Christos Comninellis, Pierre-Alain Michaud, Marco Panizza

The electrochem. behavior of a synthetic B-doped diamond thin film electrode (BDD) was studied in acid media contg. phenol using cyclic voltammetry and bulk electrolysis. In the potential region of H2O stability direct electron transfers can occur on BDD surface resulting in electrode fouling due to the formation of a polymeric film on its surface. During electrolysis in the potential region of oxygen evolution, complex oxidn. reactions can take place due to electrogenerated hydroxyl radicals. Electrode fouling is inhibited under these conditions. Depending on the exptl. conditions, the electrogenerated hydroxyl radicals can lead to the combustion of phenol or to the selective oxidn. of phenol to benzoquinone. The exptl. results also were compared to a theor. model that permits the prediction of the evolution with time of phenol concn., during its combustion, or during its selective oxidn. to benzoquinone. [on SciFinder (R)]

2002

Chargement

Promotion électrochimique des catalyseurs à base de rhodium et d'iridium

Justyna Eaves

In this thesis, the electrochemical promotion of lr and Rh based catalysts was studied for the complete combustion of ethylene and propylene. The study was performed by using two types of electrocatalytical cells: a classical, pellet type cell and a tubular cell. This work has two major goals. The first one is the optimization of the employed electrocatalytical systems from electrochemical point of view. The second one concerns the study of the mechanism of the electrochemical promotion. The major part of this work concerns the electrochemical characterization of two cell types: a pellet type cell and a tubular cell. On the basis of the obtained results the modélisation of the potential and current distribution was performed, providing key parameters for the development of more efficient cell configurations. On one hand, these configurations ensure an uniform current distribution on the working electrode and enable correct catalyst potential measurement. On the other hand, it minimizes the current bypass in the bipolar tubular cell. The aim of the investigation in a two-compartment reactor was to evaluate and to compare the Au and Ir electrodes used in this work. Under 400°C, gold was found to be much worse material than lrÛ2 both as reference and counter electrode. Its potential was affected by oxygen and propylene adsorption and no equilibrium of electrochemical reaction was obtained at such low temperature. On the base of this knowledge, several materials better adapted to electrochemical promotion conditions have been proposed. Using the two-compartment reactor potential measurements under steady state conditions allowed to verify the mechanism of the propylene combustion on Rh and that of ethylene combustion on lr based catalysts proposed in the literature. Ameliorations of the existent kinetic models were proposed. The kinetic measurements were then analyzed with the additional help of ex situ XPS analysis. This study allowed to link the oxidation state of the catalyst surface with the extent of electrochemical promotion of the catalysts. It also allowed the ex situ observation of the appearance of new oxygen (oxide) species on the gas exposed surface of Ir catalyst. This new type of oxygen was different from the oxygen of Ir02 oxide, and it can represent the promoting species, according to backspiïïover theory. The same oxygen species was observed on well oxidized Ir02 catalyst surface, even before the polarization of this catalyst. Its presence was associated to the catalyst-support effect. It explains the high activity of Ir02 catalyst by comparison with the catalytic activity of lr metal. XPS analysis of Rh based catalysts indicated the possibly formation of an inferior Rh oxide (close to RhO) due to polarization. This may be a possible explanation of the observed permanent electrochemical promotion. Voltammetric charge measurements in very narrow potential window were performed while changing the catalyst thickness. The charge was demonstrated to be proportional to the catalyst thickness, suggesting the presence of the charged species on the gas exposed catalyst surface. The analogy between this situation and that of the emerged electrodes in liquid state electrochemistry was emphasized. The voltammograms obtained in this study were interpreted in the quite new, original way, which allowed to calculate the capacity of the different catalyst interfaces, the gas/catalyst interface, and the triple phase boundary, in good agreement with reference values from impedance spectroscopy measurements. Finally, the reaction rate transients during galvanostatic polarization of lr based catalyst have been moralized. The model fits well the experimental results.

EPFL2004

Chargement

Promotion électrochimique des catalyseurs à base de rhodium et d'iridium

Justyna Eaves

EPFL2004

EPFL2008