Microstructure and mechanical properties of an ODS RAF steel fabricated by hot extrusion or hot isostatic pressing
Graph Chatbot
Chattez avec Graph Search
Posez n’importe quelle question sur les cours, conférences, exercices, recherches, actualités, etc. de l’EPFL ou essayez les exemples de questions ci-dessous.
AVERTISSEMENT : Le chatbot Graph n'est pas programmé pour fournir des réponses explicites ou catégoriques à vos questions. Il transforme plutôt vos questions en demandes API qui sont distribuées aux différents services informatiques officiellement administrés par l'EPFL. Son but est uniquement de collecter et de recommander des références pertinentes à des contenus que vous pouvez explorer pour vous aider à répondre à vos questions.
A statistical model for fracture of aligned-whisker-reinforced metals was used to interpret tensile data of a TiB-reinforced titanium alloy. From this analysis, a TiB whisker strength of 8.0 GPa with a Weibull modulus of 2 was predicted. The analysis is co ...
In the quest of materials for the first wall of the future fusion reactor, it has been shown that oxide dispersion strengthened (ODS) ferritic / martensitic (F/M) steels appear to be promising candidates. The inherent good mechanical properties supported b ...
Uniform Material Law (UML) is a handy and user-friendly method since only the tensile strength data of the material is needed for estimation of the strain-life curve, in contrast to other methods, such as four-point correlation method, universal slopes met ...
Hot tearing is one of the most severe defects observed in castings, e.g. in billets or sheet ingots of aluminum alloys produced by DC casting. It is due to both tensile strains and a lack of interdendritic feeding in the mushy zone. In order to predict thi ...
Two types of oxide dispersion strengthened (ODS) ferritic steels, with the composition of Fe-14Cr-2W-0.3Ti-0.3Y(2)O(3) (in weight percent), have been produced by mechanically alloying elemental powders of Fe, Cr, W, and Ti with Y2O3 particles either in arg ...
Uniaxial quasi-static tensile testing on individual nanocrystalline Co nanowires (NWs), synthesized by electrochemical deposition process (EDP) in porous templates, was performed inside a scanning electron microscope (SEM) using a microfabricated tensile s ...
During cold forming processes materials are subjected to non-monotonic complex multiaxial loadings. To obtain complex shapes at low temperature requires the use of particularly ductile materials. The damage behaviour of two ductile steels is studied here a ...
Thick-film materials are very advantageous for piezoresistive pressure and force sensors because of ease of processing, reliability and low cost. The standard substrate material used with thick-film technology for sensing is alumina, but its elastic modulu ...
A fairly simple experimental setup has been designed for testing the resistance of the mushy zone of alloys during solidification under tensile conditions. It has been used to study the effect of coalescence among the solid grains at a late stage of solidi ...
The tensile mechanical response of three semi-solid as-cast aluminum alloys - AA3104, AA6111, and CA31218 (an alloy similar in composition to AA3003) - was measured between a fraction solid f(s) similar to 0.85 and f(s) similar to 1 in order to establish t ...