Electrochemical Investigation of the O-2(g),Ni/YSZ System Using Cyclic Voltammetry

Christos Comninellis, Cyril Falgairette
2010
Article

Résumé

Cyclic voltammetry was used for the electrochemical study of a Ni thin film (similar to 880 nm) deposited on an yttria-stabilized zirconia (YSZ) solid electrolyte pellet at temperatures between 350 and 450 degrees C at 20 kPa O-2 and atmospheric pressure. NiO formed electrochemically by the O2- species supplied from the electrolyte upon anodic polarization, while it grew according to the parabolic growth law, in agreement with Wagner's oxidation theory of metals at high temperatures. A model for the NiO formation was proposed, where NiO is formed at the Ni/YSZ interface and grows by the outward diffusion of Ni2+ species through NiO, which is determined as the rate-limiting step. This implies the autoinhibition of NiO formation by its continuous growth. The above result agrees with Wagner's theory; however, a difference between the latter and the current model is the means of supplying oxygen for NiO formation. Also, O-2 evolution reaction is not firmly affected by NiO formation because it is controlled by the electronic current. An apparent activation energy of the limiting Ni2+ diffusion step was calculated to be 35 kJ/mol under 400 mV and decreased with potential increase.

Official source

https://infoscience.epfl.ch/record/172751?ln=fr

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Concepts associés

Chargement

Publications associées

Chargement

Effectiveness factor of thin-layer IrO2 electrocatalyst

Erika Herrera Calderon

Dimensionally Stable Anodes (DSA®) are electrodes composed of a metal support and an oxide coating (catalyst). Particularly in this thesis, the Ti/IrO2 electrode was used for the study of the fraction of the surface which participates effectively in the investigated reactions (effectiveness factor, Ef ). Four reactions with different kinetics have been investigated: (a) Fe3+/Fe2+ (fast reaction), (b) O2 and (c) Cl2 evolutions (slow reactions), and (d) isopropanol oxidation (complex reaction involving redox catalysis). This study has allowed us to apply for the first time in electrocatalysis the term, effectiveness factor, Ef , used before in other fields like in heavy metals recovery with 3D electrodes and in heterogeneous catalysis. On the other hand, in order to achieve the main objective of this thesis, an analytical and a qualitative approach was proposed. Furthermore, the Ti/IrO2 electrodes were characterized electrochemically using the cyclic voltammetry (CV) technique in which the voltammetric charge was measured at different potential scan rates, potential windows, and electrolyte temperatures using various Ti/IrO2 loadings. From the voltammetric charge, two contributions were found. The first contribution is related to the double layer capacitance and the second with the redox couples present on the electrode surface. The first reaction investigated in this work was the Fe3+/Fe2+ redox couple. In the first part of the investigation of this reaction, the CV technique was used; however, some issues related to the uncompensated electrolyte resistance were encountered. Therefore the effectiveness factor for this particular case was not possible to obtain. On the other hand, using rotating Ti/IrO2 disk electrodes (RDE) for the same reaction, the effectiveness factor, Ef , has been estimated, however, this value is much lower than the predicted one. The other investigated reactions in this work were O2 and Cl2 evolutions. The investigated kinetics of both reactions showed that the evolution of chlorine is much faster than that of oxygen. The effectiveness factor, Ef , for the oxygen evolution was close to the unity for all IrO2 loadings, contrary to the chlorine reaction that decreased with the loading. This behaviour was predicted according to what is given in the analytical approach. The last reaction investigated in this work was the oxidation of isopropanol. In this case a model was proposed based on three main reactions: Electrochemical IrO2 oxidation to IrO3, chemical oxidation of isopropanol via IrO3, and chemical decomposition of IrO3 to IrO2. The effectiveness factor, for the electrochemical reaction seemed not to correlate with the loading, whereas for the chemical one, it diminished with the loading.

EPFL2008

Chargement

The chemical and electrochemical promotion of highly dispersed nanofilm Rh catalysts (dispersion: about 10 %, film thickness: 40 nm) has been investigated for the first time. To this end Rh metal was sputter-deposited, either on a purely ionic conductor (8 % Y2O3-stabilized ZrO2) or on a mixed ionic-electronic conductor (TiO2), the latter being a highly dispersed layer of TiO2 (4 µm) deposited on YSZ. These catalysts are designated as Rh/YSZ and Rh/TiO2/YSZ, respectively. It was established analytically that both in the Rh/YSZ and in the Rh/TiO2/YSZ system, the catalyst films have a nanoparticle-size grain structure. The Rh supported on titania is rather porous, exhibiting a higher dispersion and surface area than Rh on YSZ. Both after reduction (H2, T=400 °C) and after oxidation (O2, T=400 °C), Rh supported on TiO2 was found to be in a more highly reduced state than Rh on YSZ. After reducing treatment, the Rh/TiO2/YSZ samples contain a larger amount of weakly bonded oxygen, which can be attributed to oxygen "backspillover" from the TiO2. A major feature of this research was the electrochemical characterization of the oxygen/Rh/solid electrolyte three-phase boundary by steady-state polarization measurements and by impedance spectroscopy. These are powerful techniques for extracting experimental trends and details that are useful for an understanding of the electrochemical promotion principles. It was shown that the exchange current densities at the Rh/solid electrolyte interface are lower on account of the TiO2 layer. The exchange current densities are more than twice lower at Rh/TiO2(4 µm)/YSZ than at Rh/YSZ, demonstrating that the former interface is much more polarizable. The mechanism of oxygen exchange occurring close to equilibrium (O2/O2- couple) was investigated for the first time at Rh catalyst electrodes interfaced with solid electrolyte. The processes of cathodic oxygen reduction and anodic oxygen evolution are not symmetric, but they are similar in the two systems, Rh/YSZ and Rh/TiO2(4 µm)/YSZ. The cathodic process consists of three steps: dissociative adsorption of oxygen at the gas-exposed Rh surface, atomic oxygen diffusion to the electrochemical reaction sites (ERS), and a two-electron transfer to this oxygen on the ERS. The cathodic process is limited by interfacial diffusion of oxygen atoms from the gas-exposed metal surface to the ERS. The anodic process includes two steps: two-electron transfer reaction, which is the rate-determining step, and oxygen desorption to the gas phase. With data obtained from impedance spectroscopy at the equilibrium potential, it was possible to confirm the reaction scheme proposed. It was demonstrated that Rh nanofilm catalysts interfaced with YSZ or TiO2/YSZ can be electrochemically promoted for the reaction of ethylene oxidation. Small anodic currents cause periodic oscillations in catalytic rate and potential of the Rh/YSZ catalyst, while at Rh/TiO2/YSZ they give rise to a stable and reversible rate enhancement by up to a factor 80. The increase in ethylene oxidation rate is up to 2000 times larger than the electrochemical rate, I/2F, of O2- oxidation. The pronounced electrochemical promotion behavior that has been observed is due to the anodically controlled migration of O2- species from the electrolyte to the Rh/gas interface. At the Rh surface, these species destabilize the formation of rhodium surface oxide (Rh2O3). The existence of backspillover oxygen species has been confirmed by impedance measurements under positive applied potential. Another significant result for heterogeneous catalysis is the finding that thick as well as thin films of Rh/TiO2/YSZ catalyst are open to chemical promotion of ethylene oxidation and partial methane oxidation, ie, they offer a higher catalytic activity and stability than the Rh/YSZ catalysts. The modification of catalytic activity observed for Rh/TiO2/YSZ was attributed to either a "long-range" electronic-type SMSI mechanism or to a self-driven electrochemical promotion mechanism. In both cases, the ultimate cause of promotion are different work functions of catalyst and support. Equilibration of the work functions of two solids in contact induces surface charging, a migration of O2- ions to the catalyst/gas interface, and a weakening of the Rh-O chemisorptive bonds. It facilitates reduction of oxidized surface sites. Another important achievement of the present work was that of exploring and confirming the possibilities of current-assisted activation of Rh/TiO2/YSZ catalysts. In partial methane oxidation using close to stoichiometric gas compositions (CH4 : O2 = 2 : 1) at 550 °C, the inactive (oxidized) Rh/TiO2/YSZ catalyst was successfully activated by applied currents, either positive or negative. This phenomenon is an example of "permanent" electrochemical promotion furnishing a permanent rate enhancement ratio of γ = 11. The activation by negative currents is explained in terms of an electrochemical reduction of rhodium surface oxide, while the activation by positive currents can be explained by the mechanism of electrochemical promotion.

EPFL2005

Chargement

Electrochemical promotion of Pt catalysts for gas phase reactions

Arnaud Jaccoud

The subject of this work is the study of the electrochemical promotion of catalysis (EPOC), also called non-Faradaic electrochemical modification of catalytic activity (NEMCA). In this phenomenon, application of small currents or potentials on catalysts in contact with solid electrolytes leads to very pronounced strongly non-Faradaic and reversible changes in catalytic activity and selectivity. This work concerns the system composed of platinum film electrodes, deposited on the YSZ electrolyte (ZrO2 doped with 8% Y2O3), in contact with an oxygen containing atmosphere (the O2(g),Pt/YSZ system). The aim of this work was to focus on two points in the phenomenon of EPOC: 1) The nature of the species present on the surface of the catalyst and their impact on the catalytic activity. 2) The phenomenon of permanent promotion of catalysis (P-EPOC), for which the catalytic rate enhancement is not totally reversible, leading to a long lasting activated state. The Pt electrodes were prepared via three different methods (sputtering, thermal decomposition and screen-printing) and, as expected, the resulting microstructure, observed by scanning electron microscopy (SEM), was found to depend greatly on the preparation technique. The electrochemical response of each electrode was characterized by the technique of cyclic voltammetry. Due to the occurrence of different site-related electrochemical reactions, the voltammogram shape was highly influenced by the microstructure of the Pt/YSZ contact. Based on the preliminary studies, the cermet electrode was chosen for additional electrochemical experiments, using chronoamperometry, chronopotentiometry, cyclic voltammetry, steady state polarization and impedance spectroscopy. The results of all these techniques suggest that under anodic polarization, two parallel reactions take place. The first reaction is the oxygen evolution, giving rise to a steady state current under a constant applied potential. The other reaction is the oxygen storage (oxygen injection) in the form of Pt-O species. This second process gives rise to a time dependant current under a constant applied potential, and is therefore responsible for the pseudocapacitive behavior of the electrode. Moreover, linear sweep voltammetry measurements indicated that, by application of an anodic potential, at least three types of Pt-O species were stored, following distinct kinetics. Based on the amount of stored Pt-O and on the corresponding storage kinetics, they were attributed to three different locations on the electrode: 1) at the Pt/YSZ interface, 2) diffusing from the tpb toward the Pt/gas interface, 3) diffusing from the Pt/YSZ interface toward the bulk of the platinum electrode. It has been shown that the Pt film exhibited various activity states toward the catalytic oxidation of ethylene, depending on the oxygen species present at its surface. As evidenced by XPS measurements and in agreement with the thermodynamic data for the given system, the inactive (deactivated) state has been attributed to the formation of surface platinum oxide at T > 550°C. Decreasing the reaction temperature to 525°C caused the slow spontaneous reactivation of the catalyst and several days were necessary to reach the active state, where most of the catalyst was present in its metallic state. The catalyst activity recovery could be accelerated by the application of anodic potential pulses. In agreement with the mechanism of EPOC, this was explained by the oxide destabilizing effect of the anodically produced Oδ- species. Anodic polarization also caused reversible electrochemical promotion of catalysis at unusual high temperature (600°C). In addition, very intriguing catalytic relaxation transients were observed after prolonged anodic polarization times. Indeed, it was found that enhanced catalytic activity could be maintained for up to 10 hours after current interruption. Combination of these latter results, the related literature, the state of the art model of EPOC, and the results obtained by electrochemical techniques led to the proposition of an original model based on the processes of Pt-O storage/release at various locations of the O2(g),Pt/YSZ system. According to this model, anodic polarization produces Oδ- back-spillover species, promoting the catalytic activity, in agreement with the mechanism of EPOC. In parallel, hidden oxygen species are stored at the Pt/YSZ interface and diffuse toward the Pt phase. When the polarization is switched off, these hidden oxygen species diffuse to the gas-exposed surface and cause non-Faradaic promotion, as back-spillover Oδ- do. The large amount of stored charge and its slow diffusion controlled emergence causes the rate enhancement to last for hours.

EPFL2007

Chargement

Effectiveness factor of thin-layer IrO2 electrocatalyst

Erika Herrera Calderon

EPFL2008

EPFL2005

Electrochemical promotion of Pt catalysts for gas phase reactions

Arnaud Jaccoud

EPFL2007