An examination of catalyst deactivation in p-chloronitrobenzene hydrogenation over supported gold

The stability of Au/Al2O3 in the continuous gas phase (423 K) hydrogenation of p-chloronitrobenzene (p-CNB) to p-chloroaniline (p-CAN) has been investigated over an inlet H-2/p-CNB = 4-390, i.e. from close to stoichiometry to H2 far in excess. The catalyst (activated unused and spent) has been characterised with respect to specific surface area (SSA)/porosity, temperature programmed reduction (TPR), powder XRD, H-2 chemisorption, STEM, XPS, elemental analysis and TGA-DSC measurements. Activation of Au/Al2O3 by TPR in hydrogen generated a narrow Au size distribution (1-8 nm, mean = 3.6 nm) with evidence (from XPS) of (support -> metal) charge transfer to generate surface Au delta-. Exclusive p-CAN production was achieved under conditions of kinetic control, which were established by parameter estimation and experimental variation of contact time, catalyst particle size and p-CNB/catalyst ratio. A temporal decline in activity was observed that was more pronounced at H-2/p-CNB

Novel catalytic applications of carbon nanofibers on sintered metal fibers filters as structured supports

Marina Ruta

Supported metal catalysts are important from both an industrial and a scientific point of view. They are used, amongst others, in large-scale processes such as catalytic reforming, hydrotreating, polymerization reactions and hydrogenations. Often, these catalysts consist of nanosized metal particles deposited on a suitable support, which acts as an anchor for the active phase and, in several cases, contributes to improve the overall catalyst performances. The growth of carbon nanofibers on sintered metal fibers filters (CNF/SMF) by hydrocarbons catalytic decomposition results in a structured composite material presenting all the suitable characteristics for its application as catalyst support. The main objective of this thesis was to develop novel catalytic systems based on CNF/SMF as catalytic support for continuous gas-phase hydrogenations. At first, the synthesis of CNF/SMF was optimized to tailor the properties of the material for further applications as catalytic support. The use of ethylene as carbon precursor and high synthesis temperature (973K) provided high yields of well-ordered CNF with increased specific surface area (SSA), up to 516 m2/g. On the other hand, the synthesis of CNF by ethane decomposition, which is less reactive than ethylene, resulted in a support with higher permeability, minimizing the pressure drop and being more suitable in a continuous-flow reactor. After the synthesis, the CNF surface was activated by treatment with O3 or H2O2. A novel technique, which consist of XPS analysis after step-wise TPD in UHV conditions, was developed and applied for the surface characterization. It allowed to assess the nature of the functional groups created on the CNF surface. The O3-activation was found the most effective for increasing the acidity of the CNF/SMF surface, yielding a relatively high amount of carboxylic functional groups. These groups are important because involved in the chemical anchoring and stabilization of the active metal deposited on the support. Industrially, many hydrogenations are performed over supported metal catalyst. The majority of these reactions are known to be structure sensitive reactions, so the control of the metal particle size is crucial in order to study the catalyst activity and selectivity. We prepared monodisperse-sized Pd nanoparticles (8, 11 and 13 nm) via the reverse microemulsion method and deposited on CNF/SMF and activated-CNF/SMF for a two-fold study: the effect of the nanoparticles size and the effect of the support nature on the selective hydrogenation of acetylene. The antipathetic size dependence of the TOF disappeared at particle size bigger than 11 nm. The initial selectivity to ethylene (∼60%) was found size-independent. The structure-sensitivity relations have been discussed in terms of "geometric" and "electronic" nature of the size-effect and rationalized assuming a Pd-Cx phase formation which is known to be size-dependent. CNF/SMF supports with increased acidity diminished the formation of coke and changed the by-products distribution, diminishing the catalyst deactivation. Subsequently, CNF/SMF was applied to develop a new catalytic system: the Structured Supported Ionic Liquid Phase (SSILP) catalyst, embedding an active Rh complex. The selective gas-phase hydrogenation of 1,3-cyclohexadiene to cyclohexene was used as model reaction. The SSILP based on CNF/SMF supports showed a high turnover frequency, up to 250 h-1 and selectivity > 96%. Multiple advantages of supporting a homogeneous active phase, dissolved in IL, on CNF/SMF have been demonstrated: the thin layer of IL was homogeneously distributed over the mesoporous support, so mass transfer limitations could be avoided, furthermore the chemical inertness of the CNF prevented any interaction between the active phase dissolved in IL ensuring an efficient use of the Rh complex. The SSILP concept can be applied not only for the "heterogenization" of a transition metal catalyst, but also to obtain metal nanoparticles with monodispersed size via the reduction of a metal precursor dissolved in IL. In this case, IL provides a suitable environment for the nucleation and growth of the nanoparticles. By applying the SSILP concept to the selective hydrogenation of acetylene, the influence of IL on the stability of the nanoparticles was investigated. Moreover, the different solubilities of reactants and products in the IL phase allowed to improve the selectivity toward ethylene. Monodispersed Pd nanoparticles of 5 and 10 nm in SILP on CNF/SMF showed excellent long-term stability. The lower solubility of ethylene than acetylene in the IL had the beneficial effect of allowing high selectivity to ethylene up to 85%, due to the inhibition of its consecutive hydrogenation to ethane. In conclusion, a novel catalytic system for continuous-flow, gas-phase hydrogenations was conceived, taking advantage of the suitable characteristics of CNF/SMF supports. The SSILP concept, involving both homogeneous and heterogeneous active phases has been demonstrated, indicating a great potential and flexibility for continuous-flow industrial applications.

EPFL2008

Surface Reactions are Crucial for Energy Storage

Elsa Callini, Shunsuke Kato, Philippe Mauron

Reactions between gas molecules, e.g. H-2 and CO2 and solids take place at the surface. The electronic states and the local geometry of the atomic arrangement determine the energy of the adsorbate, i.e. the initial molecule and the transition state. Here we review our research to identify the surface species, their chemical state and orientation, the interaction with the neighbouring molecules and the mobility of the adsorbed species and complement the experimental results with thermodynamic modelling. The role of the Ti was found to be a bridge between the charged species preventing the individual movement of the ions including charge separation. The Ti has no catalytic effect on the hydrogen sorption reaction in borohydrides. The physisorption of molecular hydrogen is too weak at ambient temperature to reach a significant hydrogen storage density. The addition of a hydrogen dissociation catalyst to a nanoporous material with a large specific surface area may potentially enable the spillover of hydrogen atoms from the metal catalyst to the surface of the porous material and chemisorb on specific sites with a much higher binding energy compared to physisorption. The intercalation of alkali metals in C-60 fullerenes increases the interaction energy of hydrogen with the so-called metal fullerides significantly. Sterical diffusion barriers by partial oxidation of the surface of borohydrides turned out to redirect the reaction path towards pure hydrogen desorption and suppress the formation of diborane, a by-product of the hydrogen evolution reaction from borohydrides previously undetected. The combination of a newly developed gas controlling system with microreactors allows us to investigate complex reactions with small quantities of nano designed new catalytic materials. Furthermore, tip-enhanced Raman spectroscopy (TERS) will allow the investigation of the reactions locally on the surface of the catalyst and the near ambient pressure photoelectron spectroscopy enables analysis of the surfaces in ultra-high vacuum and in situ interaction with the adsorbates i.e. while the reaction takes place. This brings us in a unique position for the investigation of the heterogeneous reactive systems. The mechanism of the Ti catalysed hydrogen sorption reactions in alanates was recently established based on spectroscopic investigations combined with thermodynamic analysis of the transition states.

Schweizerische Chemische Gesellschaft2015

Nanofibres de carbone sur filtre métallique comme support catalytique structuré

Pascal Tribolet

The main objectives of this work are 2-fold : The development of a novel type of composite material based on carbon nanofibers supported on sintered metal fibers filters (CNF/SMF) and to explore the use of this material as a catalytic support for a model reaction: selective hydrogenation of acetylene. The advantages of this novel support are: Due to carbon nanofibers, it combines a graphitic structure with a high specific surface area without microporosity. Supported carbon nanofibers can be used in a fixed bed reactor without very high pressure drop. Combination of two materials with high thermal conductivity gives a composite which keeps this property. It is suitable for highly exo/endothermic reactions, diminishing temperature gradients in the catalytic bed. The synthesis of carbon nanofibers on SMF filters was carried out by ethane catalytic decomposition at 655°C directly on metallic filters. An oxidation of SMF followed by a reduction in H2 create surface roughness, leading to a larger area for CNF nucleation. The CNF formation mechanism includes several steps: it starts with carbon deposition on metallic surface followed by its diffusion into the metal leading to carbides formation. When the limit of carbon solubility is attained, a layer of carbon is formed on the surface of metallic fibers. High tension within the bulk metal leads to carbide dissociation and by phase separation to graphite formation, which pushes the metallic particles through the carbon layer. Nickel, stainless steel an Inconel (an alloy of mainly nickel, iron and chromium) filters were used. The latter gave the highest uniformity of the carbon nanofibers layer showing an excellent mechanical stability. In order to control carbon deposition on the filters, a formal kinetic analysis of the decomposition reaction was undertaken. Partial orders of 1 for ethane, -2 for hydrogen and an apparent activation energy of 235 kJ/mol were obtained. The observed kinetics suggests strongly that the C – C bond scission is the rate determining step and not carbon diffusion into the metal which is often reported in the literature. The synthesis procedures like time on stream and reaction temperature were optimized: 1 hour of a mixture C2H6:H2:Ar (3:17:80) decomposition over SMFInconel at 655°C lead to ∼6% of carbon, leading to a CNF layer of 1 µm thickness covering the metallic fibers entirely. This material presents a high specific surface area (22.2 m2/g) and a low pressure drop for the gas flowing through. The carbon nanofibers have a diameter between 20 and 50 nm and a crystalline structure with platelets morphology where the graphene layers are stacked one above the other. Their surface is composed almost exclusively of carbon and hydrogen. Amongst the multiple possible applications of this novel composite material, its use as a catalyst support was assessed. Selective hydrogenation of acetylene was carried out over palladium supported on CNF/SMF and compared with commercial supports (ACF, EGF and AGF). The activated carbon fibers cloth (ACF) led to a Pd activity at least twice as E-type glass fibers tissue (EGF) or EGF covered by an alumina layer (AGF). Reaction kinetics was studied for Pd/ACF, leading to acetylene and hydrogen partial orders of -0.5 and 2.4, respectively and apparent activation energy of 50 kJ/mol. The negative partial order for C2H2 suggests high adsorption strength of this compound compared to other reagents on palladium. This particularity allows Pd to be selective. Hydrogenations are known to be structure sensitive. Therefore the catalyst activity for the model reaction depends on Pd particle size. It increases for large particle sizes. The control of this parameter was a priority. Variations of the palladium precursor, of the support and catalyst treatment were carried out. Micro-wave plasma was used since it is fast and has low energy consumption allowing chemically modifying the carbon support surface and activating catalyst after impregnation. This controls not only palladium sintering, but also decomposes tetraaminopalladate more efficiently, resulting in a catalyst activity of one order of magnitude higher. In order to control the palladium deposition on CNF/SMFInconel composite, it is important to have surface functional groups. The activation of carbon nanofibers was carried out with a 4 hours treatment in a boiling aqueous solution of hydrogen peroxide. This led to an amount on surface oxygen containing groups, per mass of carbon, higher than in ACF. Palladium particle size on the composite was controlled by support activation, the use of several metal precursors or different loadings or by a thermal treatment in argon at 500°C. Optimisation of the procedure allowed to obtain in a controlled way an average palladium particle sizes between 3.6 and 25 nm. The activity and selectivity towards ethylene of Pd/CNF/SMFInconel were observed to be higher compared to palladium supported on activated carbon, alumina or barite. Graphitic nature of carbon nanofibers, leading to strong metal-support interaction, was accounted as responsible for these improvements. The high thermal conductivity of the composite CNF/SMF ensured good heat transfer released due to the exothermicity of the reaction and allowed to work close to isothermal conditions in the catalytic bed. Finally it can be concluded, that for the first time carbon nanofibers synthesis was carried out in one step on sintered metal fibers filters, resulting in a novel structured composite material combining different specific properties and having promising potential applications.

EPFL2006