Temperature and field dependence of magnetic domains in La1.2Sr1.8Mn2O7

Amer Physical Soc, 2015
Article

Résumé

Colossal magnetoresistance and field-induced ferromagnetism are well documented in manganite compounds. Since domain wall resistance contributes to magnetoresistance, data on the temperature and magnetic field dependence of the ferromagnetic domain structure are required for a full understanding of the magnetoresistive effect. Here we show, using cryogenic magnetic force microscopy, domain structures for the layered manganite La1.2Sr1.8Mn2O7 as a function of temperature and magnetic field. Domain walls are suppressed close to the Curie temperature T-C, and appear either via the application of a c-axis magnetic field, or by decreasing the temperature further. At temperatures well below T-C, new domain walls, stable at zero field, can be formed by the application of a c-axis field. Magnetic structures are seen also at temperatures above T-C : these features are attributed to inclusions of additional Ruddleston-Popper manganite phases. Low-temperature domain walls are nucleated by these ferromagnetic inclusions.

Official source

https://infoscience.epfl.ch/record/208213?ln=fr

À propos de ce résultat

Cette page est générée automatiquement et peut contenir des informations qui ne sont pas correctes, complètes, à jour ou pertinentes par rapport à votre recherche. Il en va de même pour toutes les autres pages de ce site. Veillez à vérifier les informations auprès des sources officielles de l'EPFL.

Concepts associés

Chargement

Publications associées

Chargement

Magnetization Reversal Dynamics in Ferromagnetic Semiconductors

Liza Herrera Diez

This thesis is dedicated to the study of the magnetization reversal dynamics in compressively strained (Ga,Mn)As and differently functionalized (Ga,Mn)As materials. In the first part the domain wall dynamics of pure (Ga,Mn)As/GaAs materials is in the focus. The changes in the magnetic anisotropy energy landscape occurring as a function of temperature are monitored in detail by different experimental techniques. These measurements provide the necessary information for the identification of the temperature ranges corresponding to different magnetic anisotropy regimes. Knowing the biaxial anisotropy and uniaxial anisotropy dominated regimes the dependence of the domain wall dynamics on the magnetic anisotropy landscape is studied. Critical changes in domain wall alignment observed by Kerr microscopy are found upon changing from biaxial to uniaxial anisotropy. These changes could be partially attributed to the tendency of the system to minimize magnetic free poles at the domain boundaries. To complement the space resolved studies of the magnetization reversal, magnetic time relaxation effects are addressed. In particular the magnetic aftereffect in (Ga,Mn)As/GaAs is studied in detail. The irreversible aftereffect is evidenced as a critical reduction of the domain wall velocity with time under a constant applied magnetic field below coercivity. This time relaxation is tracked as a function of both time and magnetic field. The measurements show that the overall relaxation is composed of two relaxation processes acting in parallel at short and long time scales. By fitting these experimental results the values of the relaxation times of both relaxation processes were obtained. By this modeling also the values of the activation volumes for two independent (Ga,Mn)As materials are estimated. In the second part of this thesis the possibilities of tuning the electrical and magnetic properties of (Ga,Mn)As by volume and surface treatments are explored. As for the volume modification, oxygen species were incorporated into the (Ga,Mn)As films by means of exposure to an oxygen plasma. The incorporation of oxygen was evidenced by depth profile X-ray photoelectron spectroscopy. This treatment is found to weaken the ferromagnetism, visible as a reduction in the Curie temperature, and to hinder the electrical transport evidenced as an increase in the electrical resistance. In agreement with theories accounting for the hole mediated ferromagnetism in (Ga,Mn)As this behaviour was related to a hole compensation mechanism arising from the presence of oxygen impurities sitting in interstitial positions of the (Ga,Mn)As Zinc blende structure. In the last part, the modulation of the electrical and magnetic properties via surface functionalization is presented. The effects produced by the adsorption of molecular species on (Ga,Mn)As are similar to those found after oxygenation, namely a strong weakening of the magnetic properties and an increase in the values of the electrical resistance. However, in this case the distinctive feature is provided by the possibility of regulating the hole quenching effect by exploiting the additional degree of freedom provided by the chemical properties of the adsorbates. The adsorbate chosen for these experiments are dye molecules that absorb light in the visible range, in this way allowing for a light modulated interaction with the substrate. Using this concept is was possible to observe a modulation of the ferromagnetic transition temperature, the coercive field and the electrical resistance upon illumination. These observations provide a proof of principle for the realization of photo-sensitized (Ga,Mn)As devices where the magnetic properties can be regulated by light.

EPFL2011

Chargement

The aim of this thesis work was to obtain a deeper understanding of spin-dependent transport by the study of mixed effects of heat and charge currents in magnetic nanostructures. Indeed, even thermodynamics establish a relationship between both currents, no previous works were performed in this sense up to now. In order to do this, an original experimental setup was developed which allows to carry out a novel transport measurement called the thermogalvanic voltage (TGV). It measures the AC voltage response of the sample driven by an oscillatory variation of the temperature induced by a chopped laser beam focused on the nanostructure under a direct current flow. The main advantage of this new experimental setup is that it can be used to perform three different transport measurements: resistance, thermoelectrical power and TGV measurements. Furthermore, the well-defined junctions of our magnetic nanowires, in addition to the lock-in detection of signals, allows to obtain a better quality of thermoelectrical measurements than those observed by other groups. Different kind of magnetic nanowires like ferromagnetic/non-magnetic multilayers and ferromagnetic homogeneous nanowires were studied by these three different transport measurements. All these nanowires were 6μm in length and 50nm in diameter. All TGV measurements reveal a linear dependence with currents. This behaviour can be interpreted in terms of adiabatic conductivity for homogeneous nanowires and in terms of Peltier effect for multilayer nanowires produced in ferromagnetic/non-magnetic interfaces. Furthermore, the magnetic field dependence of TGV (MTGV) cannot be accounted for by GMR and MTEP effects. Therefore, a novel spin-dependent mechanism is invoked in such measurements. A simple phenomenological model, ascribed in the framework of thermodynamics of irreversible processes, was developed to explain this effect. It allows to identify this phenomena to a novel spin-dependent variable: The asymmetry of spin-mixing mechanisms (ΔL). This variable will be related to the difference of transition rates between both spin channels (τ-1+- and τ-1-+) developed in ferromagnetic material due to electron-magnon interactions. A large magnetic field dependence of TGV signals were observed in magnetic granular systems. Moreover, MTGV shows a different dependence from GMR on magnetic field, grain size and temperature. This effect is identified as a spin-mixing mechanism produced by the electron spin precession about the magnetic grain moments.

EPFL2006

Chargement

Magnetic phase diagram of the two-dimensional antiferromagnet Ni-5(TeO3)(4)Br-2

Helmuth Berger

Phase diagram of the two-dimensional antiferromagnet Ni-5(TeO3)(4)Br-2 with triangular arrangement of Ni2+ (S=1) magnetic moments within the [Ni5O17Br2] subunits has been investigated by temperature and magnetic field dependent heat-capacity, magnetization, and magnetic-torque measurements down to 1.5 K and up to 23 T. A nonzero magnetic contribution to the heat capacity observed up to 2.3T(N) is consistent with short-range magnetic ordering and the two-dimensional nature of the system. Below the Neel temperature T-N=29 K several antiferromagnetic phases were identified. The zero-field phase is characterized by a planar antiferromagnetic arrangement of the two in-layer neighboring [Ni5O17Br2] magnetic clusters within the magnetic unit cell. When the magnetic field is applied along the a(*) crystal axis, a spin-flop-like transition to a phase with a complex out-of-plane arrangement of Ni2+ (S=1) magnetic moments occurs at similar to 10 T. Using a molecular-field approach we predict that this transition will shift to higher fields with increasing temperature and that a magnetic phase with ferromagnetic ordering of [Ni5O17Br2] magnetic clusters will occur above 24 T. We ascribe the richness of the magnetic phases to strongly exchange-coupled clusters, being the basic building blocks of the investigated layered system.

2009

Chargement

Magnetization Reversal Dynamics in Ferromagnetic Semiconductors

Liza Herrera Diez

EPFL2011

EPFL2006