A probabilistic approach for assessing discontinuities in structural steel components based on Charpy-V-notch tests
Graph Chatbot
Chat with Graph Search
Ask any question about EPFL courses, lectures, exercises, research, news, etc. or try the example questions below.
DISCLAIMER: The Graph Chatbot is not programmed to provide explicit or categorical answers to your questions. Rather, it transforms your questions into API requests that are distributed across the various IT services officially administered by EPFL. Its purpose is solely to collect and recommend relevant references to content that you can explore to help you answer your questions.
The Mode I and II fracture behaviors of adhesively-bonded joints composed of pultruded glass fiber-reinforced polymer (GFRP) laminates were experimentally investigated using Double-Cantilever-Beam (DCB) and End-Loaded-Split (ELS) specimens. The large speci ...
In this work we have studied brittle fracture in high-chromium reduced activation tempered martensitic steels foreseen as structural materials for thermonuclear fusion reactors. Developing the adequate materials that can withstand the severe irradiation co ...
Fracture tests have been performed on 333 flexure hinges of various shapes machined in monocrystalline silicon by Deep Reactive Ion Etching. The results show the significant effects of stress concentration, crystalline orientation and surface treatments on ...
Hydrogen embrittlement is a pervasive mode of degradation in many metallic systems that can occur via several mechanisms. Here, the competition between dislocation emission and cleavage at a crack tip is evaluated in the presence of H. At this level, embri ...
In liquid metal spallation targets such as the MEGAPIE (the megawatt pilot experiment) target and the future ADS (accelerator driven system) spallation targets, which utilize liquid lead-bismuth eutectic (LBE) as the target material, liquid metal embrittle ...
With the occurrence of higher and more frequent axle loads, bridges are more solicited by fatigue loading. Bridge elements like deck slabs are subjected to a high number of stress cycles at relatively small stress magnitudes. The application of Fracture Me ...
This thesis is an exploration of deformation and fracture properties of a novel two-phase α2 + γ Ti46Al8Ta (at.%) alloy featuring a "convoluted" microstructure, produced by partners within a European Union project named IMPRESS. Properties of this alloy ar ...
The present work focuses on stress-corrosion mechanisms in soda-lime silica glass. Four-point beam-bending tests were performed on small specimens, measuring failure time in function of temperature and relative humidity. By using linear elastic fracture me ...
Fracture toughness tests are conducted at room temperature and 923 K (650 degrees C) on SENB (Single Edge Notched Bend) specimens of three different (alpha(2) + gamma ) TiAl-based alloys. One alloy is a conventional near fully lamellar Ti-45Al-2Mn-2Nb + 0. ...
Reliable collapse assessment of structural systems under earthquake loading requires analytical models that are able to capture component deterioration in strength and stiffness. For calibration and validation of these models, a large set of experimental d ...