Platinum nanoparticlePlatinum nanoparticles are usually in the form of a suspension or colloid of nanoparticles of platinum in a fluid, usually water. A colloid is technically defined as a stable dispersion of particles in a fluid medium (liquid or gas). Spherical platinum nanoparticles can be made with sizes between about 2 and 100 nanometres (nm), depending on reaction conditions. Platinum nanoparticles are suspended in the colloidal solution of brownish-red or black color. Nanoparticles come in wide variety of shapes including spheres, rods, cubes, and tetrahedra.
NanoparticuleUne nanoparticule est selon la norme ISO TS/27687 un nano-objet dont les trois dimensions sont à l'échelle nanométrique, c'est-à-dire une particule dont le diamètre nominal est inférieur à environ. D'autres définitions évoquent un assemblage d'atomes dont au moins une des dimensions se situe à l'échelle nanométrique (ce qui correspond au « nano-objet » tel que défini par la norme ISO précitée) ou insistent sur leurs propriétés nouvelles (dues au confinement quantique et à leur surface spécifique) qui n'apparaissent que pour des tailles de moins d'une centaine de nanomètres.
Nano-argentvignette|Nanoparticules d'argent, vues au microscope électronique. Le est un nanomatériau à base d'atomes d'argent, produit sous forme de nanoparticules par des nanotechnologies. En solution, il porte le nom d'. En 2008, selon les producteurs, environ /an de nano-argent auraient déjà été produites dans le monde, sous forme d'ions argent, de particules d’argent protéinées (silver proteins) ou de colloïdes utilisés comme biocide.
Nanoparticle–biomolecule conjugateA nanoparticle–biomolecule conjugate is a nanoparticle with biomolecules attached to its surface. Nanoparticles are minuscule particles, typically measured in nanometers (nm), that are used in nanobiotechnology to explore the functions of biomolecules. Properties of the ultrafine particles are characterized by the components on their surfaces more so than larger structures, such as cells, due to large surface area-to-volume ratios. Large surface area-to-volume-ratios of nanoparticles optimize the potential for interactions with biomolecules.
Polymèrevignette|Fibres de polyester observées au Microscopie électronique à balayage. vignette|La fabrication d'une éolienne fait intervenir le moulage de composites résines/renforts. Les polymères (étymologie : du grec polus, plusieurs, et meros, partie) constituent une classe de matériaux. D'un point de vue chimique, un polymère est une substance composée de macromolécules et issue de molécules de faible masse moléculaire. Un polymère est caractérisé par le degré de polymérisation.
Nanomaterial-based catalystNanomaterial-based catalysts are usually heterogeneous catalysts broken up into metal nanoparticles in order to enhance the catalytic process. Metal nanoparticles have high surface area, which can increase catalytic activity. Nanoparticle catalysts can be easily separated and recycled. They are typically used under mild conditions to prevent decomposition of the nanoparticles. Functionalized metal nanoparticles are more stable toward solvents compared to non-functionalized metal nanoparticles.
Thermoset polymer matrixA thermoset polymer matrix is a synthetic polymer reinforcement where polymers act as binder or matrix to secure in place incorporated particulates, fibres or other reinforcements. They were first developed for structural applications, such as glass-reinforced plastic radar domes on aircraft and graphite-epoxy payload bay doors on the Space Shuttle. They were first used after World War II, and continuing research has led to an increased range of thermoset resins, polymers or plastics, as well as engineering grade thermoplastics.
NanocompositeUn nanocomposite est un matériau solide multiphasé dont une des phases a au moins une dimension inférieure à . Un nanocomposite est généralement la combinaison d’une matrice massive avec une phase de renfort nanométrique de propriétés différentes résultantes des différences structurales et chimiques. Les propriétés mécaniques des nanocomposites sont différentes de celles des matériaux composites traditionnels à cause d’un rapport surface/volume élevé du renfort, et de son facteur de forme important.
Heterogeneous gold catalysisHeterogeneous gold catalysis refers to the use of elemental gold as a heterogeneous catalyst. As in most heterogeneous catalysis, the metal is typically supported on metal oxide. Furthermore, as seen in other heterogeneous catalysts, activity increases with a decreasing diameter of supported gold clusters. Several industrially relevant processes are also observed such as H2 activation, Water-gas shift reaction, and hydrogenation. No gold-catalyzed reaction has been commercialized.
Self-assembly of nanoparticlesNanoparticles are classified as having at least one of three dimensions be in the range of 1-100 nm. The small size of nanoparticles allows them to have unique characteristics which may not be possible on the macro-scale. Self-assembly is the spontaneous organization of smaller subunits to form larger, well-organized patterns. For nanoparticles, this spontaneous assembly is a consequence of interactions between the particles aimed at achieving a thermodynamic equilibrium and reducing the system’s free energy.